This paper presents an investigation into the flexural behaviour of basalt FRP reinforced concrete beams through experimental and analytical methods. To achieve the research objectives, four concrete beams reinforced with steel and four identical concrete beams reinforced with BFRP bars were tested under four-point bending. The main parameters examined under the tests are the type of concrete (lightweight foam glass concrete and normal concrete) and the type of longitudinal reinforcement bars (BFRP and steel). Test results are presented in terms of failure modes; deformation crack pattern and the ultimate moment of resistance are presented. The experimental results are analysed and compared to predictive models proposed by ACI 440.1R, 2006 and BS EN 1992, Eurocode 2, for deformations and ultimate flexural capacities of the steel and BFRP reinforced concrete beams. The experimental results indicated that the flexural capacity decreased for the beams reinforced with BFRP bars compared to that of a corresponding beam reinforced with steel bars. Both types of beams failed in the modes predicted. The prediction models underestimated the flexural capacity of BFRP reinforced concrete beams. The increase in foam glass aggregate content was observed to reduce the cracking load by almost 10 - 40% and 25 - 50% for steel and BFRP reinforced concrete beams, respectively. The flexural capacities of BFRP reinforced beams were underestimated by using equations stipulated in ACI 440.1R and Eurocode 2 codes of practice.

This paper presents a numerical investigation on the flexural performance of a novel cementitious reinforced GEM-TECH material using finite element method. A discrete nonlinear FE model using the commercial software ANSYS was employed to model a steel-reinforced GEM-TECH beam. Element SOLID65 was used to model the cementitious material while LINK180 element was used to model the reinforcing bars and stirrups. For model validation, FEA results and crack plots were compared to those obtained from the experimental results of five reinforced GEM-TECH beams: three beams designed with target density of 1810 kg/m3 and two beams with target density of 1600 kg/m3. Both load-deflection plots and the failure mode crack plots predicted by the FE model were in good agreement with the experimental results.