The chitosan-coated neem flower powder was prepared and employed as an adsorbent for the removal of cationic methylene blue from an aqueous medium. The interaction of chitosan with neem flower was concluded by FTIR. The BET surface area was evaluated for the prepared NFC adsorbent. The adsorption of methylene blue dye onto chitosan-coated neem flower powder (bio-adsorbent) was carried out by varying the concentration of dye, pH, temperature and concentration of adsorbent. The adsorption capacity was evaluated by using Freundlich and Langmuir models. The adsorption data were further analysed with the help of pseudo-first and second-order kinetic models. The thermodynamic parameters were evaluated to comprehend the nature of the adsorption process.

In this work, novel cellulosic fibers are extracted from Washingtonia Filifera (WF) plant using an environment friendly technique. Morphological, physico-chemical, thermal and mechanical properties are reported in this paper. Micro graphical SEM shows the presence of cells in the fiber. FTIR and XRD experimental analyzes show a cristinality index of 48.88%, and the WF fibers are found to be thermally stable until 201°C by using TGA and DTG thermo graphic analyzes with an appropriate activation energy of 72.46 kJ/mol, where Young modulus and tensile strength of strain were determined using tensile tests of single fiber at 2.17 GPa, 134 MPa and 26.55%, respectively. Mechanical properties are analyzed using a statistical method.

HDPE was functionalized with two different esters in an inert atmosphere at 160°C, under different experimental conditions by thermolysis method. The order of the functionalization and crosslinking reactions was determined. The C=C formation peak is assigned at 1610 cm-1.The percentage of functionalization was determined by FTIR spectroscopy method. Thermogravimetric analysis and differential scanning calorimetric methods were also used to study about the thermal properties of the functionalized HDPE.