This paper presents an experimental investigation on cutting temperature during hard turning of EN 24 steel (50 HRC) using TiN coated carbide insert under dry environment. The prediction model is developed using response surface methodology and optimization of process parameter is performed by desirability approach. A stiff rise in cutting temperature is noticed when feed and cutting speed are elevated. The effect of depth of cut on cutting temperature is not that much significant compared with cutting speed and feed as observed from main effects plot. The response surface second order model presented high correlation coefficient (R2 = 0.992) explaining 99.2 % of the variability in the cutting temperature which indicates the goodness of fit for the model to the actual data and high statistical significance of the model. The experimental and predicted values are very close to each other. The calculated error for cutting temperature lies between 1.88-3.19 % during confirmation trial. Therefore, the developed second order model correlates the relationship of the cutting temperature with the process parameters with good degree of approximation. The optimal combination for process parameter is depth of cut at 0.2mm, feed of 0.1597 mm/rev and cutting speed of 70m/min. Based on these combination, the value of cutting temperature is 302.950C whose desirability is one.

The objective of the study is to assess the performance of multilayer coated carbide insert in the machining of hardened AISI D2 steel (53 HRC) using Taguchi design of experiment. The experiment was designed based on Taguchi L27 orthogonal array to predict surface roughness. The S/N ratio and optimum parametric condition are analysed. The analysis of variance has also been carried out to predict the significant factors affecting surface roughness. Based on Taguchi S/N ratio and ANOVA, feed is the most influencing parameter for surface roughness followed by cutting speed whereas depth of cut has least significant from the experiments. In regression model, the value of R2 being 0.98 indicates that 98 % of the total variations are explained by the model. It indicates that the developed model can be effectively used to predict the surface roughness on the machining of D2 steel with 95% confidence intervals.

Turning hardened component with PCBN and ceramic inserts have been extensively used recently and replaces traditional grinding operation. The use of inexpensive multilayer coated carbide insert in hard turning is lacking and hence there is a need to investigate the potential and applicability of such tools in turning hardened steels. An attempt has been made in this paper to have a study on turning hardened AISI 4340 steel (47 ± 1 HRC) using coated carbide inserts (TiN/TiCN/Al2O3/ZrCN) under dry environment. The aim is to assess the tool life of inserts and evolution of flank wear with successive machining time. From experimental investigations, the gradual growth of flank wear for multilayer coated insert indicates steady machining without any premature tool failure by chipping or fracturing. Abrasion is found to be the dominant wear mechanisms in hard turning. Tool life of multilayer coated carbide inserts has been found to be 31 minute and machining cost per part is Rs.3.64 only under parametric conditions chosen i.e. v = 90 m/min, f = 0.05 mm/rev and d = 0.5 mm. The mathematical model shows high determination coefficient, R2 (99%) and fits the actual data well. The predicted flank wear has been found to lie very close to the experimental value at 95% confidence level. This shows the potential and effectiveness of multilayer coated carbide insert used in hard turning applications.