The article discusses the strength of concrete and other brittle materials in the case of non-uniform biaxial type of compression (σ1 > σ2 > 0) and triaxial compression of σ1 > σ2 = σ3 > 0 type (it was assumed that σ> 0 corresponds to compression). It is noted that, when considering the biaxial loading in the accepted model, probabilistic nature of distribution of stresses along the contour of pores and inclusions, i.e. stress causing formation and propagation of cracks in the material, plays an important role. Moreover, the stress across the circuit pores was regarded as a three-dimensional random field of S(α,β,γ,ω),where ω - is a random argument. Considering the average number of overshoots NR we believed that the random field of S is not homogeneous (not stationary): its expectation is not constant, but is a function of nonrandom arguments Мs = Мs(α;β;γ). External load, corresponding to NR = const (and at the same time constant of level exceedance probability), first increases and then decreases a little. Heating up to 300оС (573K) and 400оС (673K) leads to violations, and long-term load leads to significant changes in the macro- and microstructure of concrete.

The article is devoted to some aspects of research of hostile environment influence on the concrete durability. The mechanism of formation of chaotically diversified difficult structure is described. Chemical interactions of cement with active components of diffusion in steam space are examined. Measures for receiving conditions under which the volume of products of reaction will be equal to the volume of the reacted alkaline components of a cement stone are offered. High-quality and quantitative changes in a pore space, which are irrespective of density and the relative molecular mass of reaction products are described. Besides, movement and distribution of gaseous products of reaction in volumes of a cement stone are simulated. Reasonable integrated dependences of influence of aggressive environment on various types of concrete surfaces are given. The methods of corrosion control offered in article allow substantially to lower or absolutely to exclude adverse effect of hostile environment on concrete and reinforced concrete structures already at a stage of selection of composition of concrete mix. In this case service life of concrete and reinforced concrete structures will increase.